BIOMIMETIC HYDROXYAPATITE COATING ON C.P. Ti AND Ti-6Al-4V ALLOY BY ACID AND ALKALI TREATMENT
Autori: Chao-Lun Fu, Hsueh-Chuan Hsu, Shih-Ching Wu, Shih-Kuang Hsu, Wen-Fu Ho
Data aparitiei: November/2011
Revista: Environmental Engineering and Management JournalVol. 10Nr. 11
ISSN: 1843 - 3707
Pret: Gratuit    
Format PDF Format PDF
Abstract:

Titanium metal and its alloys have been widely used as implants under load-bearing conditions due to their biocompatibility, excellent corrosion resistance and lightness, but their inability to bond to living bone is a setback. The experiments outlined here investigated hydroxyapatite (HA) coating on Ti metal implants, used to enhance their bioactive properties. In this study, specimens of commercially pure titanium (c.p. Ti) and Ti-6Al-4V were etched in either H3PO4 or HCl, and subsequently treated in 15 M NaOH. The surfaces of acid-etched c.p. Ti showed a porous structure while those of acid-etched Ti-6Al-4V showed some grinding marks, but no porosity. After subsequent alkali treatment in NaOH, the surfaces of both c.p. Ti and Ti-6Al-4V substrates exhibited microporous network structures composed of Na2Ti5O11. The pre-treated specimens were then immersed in simulated body fluid (SBF) at 37 °C up to 14 days. HA began to deposit on acid-etched and NaOH-treated Ti-6Al-4V within a day of immersion in SBF. After 14 days of immersion in SBF, a dense and uniform layer was produced on the surfaces of acid-etched and NaOH-treated Ti-6Al-4V. The HA formation rate was the highest for HCl and NaOH pre-treated samples. Thus, this method of HA coating on c.p. Ti and Ti-6Al-4V shows promise in its application for artificial bone substitutes or other hard tissue replacement materials with heavy load-bearing requirements. Aside from their desirable combination of bioactivity, they also exhibit excellent corrosion resistance and their processing costs are low.


Sus

Acasa · Carti editate · Reviste · Despre editura · Abonament · Contact · Cos cumparaturi · Cum platesc? · Termeni si conditii
VisaMaster CardPayU

2001 - 2024 © Copyright Editura EcoZone Iasi Toate drepturile sunt rezervate.
Gazduire skaleweb.ro

SkaleWeb